SENG OKSIDA (ZnO) SEBAGAI FOTOKATALIS PADA PROSES DEGRADASI SENYAWA BIRU METILEN Darajat, Syukri; Aziz, Hermansyah; Alif, Admin
Jurnal Riset Kimia Vol 1, No 2 (2008): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v1i2.72

Abstract

 ABSTRACT A research aimed to study the influence of ZnO white powder on photodegradation of methylene blue using Merkuri lamp (l = 365 nm) as light source have been reached. A suspension of ZnO (40 mg) mixed with 25 mL of methylene blue solution (initial concentration of 0.015 mM) then was illuminated for 60 minutes showed degradation and quantum yield amounting 23.84% and 3.55 molecules photon-1, respectively. These results mean that by using ZnO as photocatalyst there is about four times efficiency than the one without ZnO either in case of time consumed or the number of photon applied. In kinetic study, it has been observed that such semiconductor-catalyzed photochemical reaction obeys the first order rule where rate constant and half time consecutively were 0.0029 minute-1 and 231 minutes.  Keywords : photodegradation, photocatalyst, quantum yield, semiconductor, photochemical reaction.
OPTIMALISASI TRANSPORT SELEKTIF ION Ni(II) TERHADAP Cd(II) DENGAN ZAT PEMBAWA OKSIN MELALUI TEKNIK MEMBRAN CAIR FASA RUAH SECARA SIMULTAN Ningsih, Vera Tri; Alif, Admin; Aziz, Hermansyah
Jurnal Riset Kimia Vol 2, No 2 (2009): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v2i2.159

Abstract

  ABSTRACT The selective transport of Ni(II) to Cd(II) through simultaneously liquid membrane technique has been investigated. The cell membrane was made by mixturing Ni(II) and Cd(II) ions at concentration as 3.41x10-4 M and 1.78x10-4 M respectively as source phase, oxine in chloroform as membrane phase and Na2EDTA solution as receiving phase. Concentration of recidual Ni(II) and Cd(II) ions in source phase transported to receiving phase was measured by Atomic Absortion Spectrofotometry (AAS). The results showed the at optimum condition of Ni(II) and Cd(II) transport occurred at source phase of pH 7, oxine concentration 0.001 M in chloroform and 0.04 M Na2EDTA solution pH 7. In this condition, Ni(II) and Cd(II) transport selectivity was found 80.89%. From the experiment, it was found that the transport rate constant from source phase to membrane phase (k1) for Ni(II) (0.7544 per hour) smaller than Cd(II) (1.3800 per hour ), on the other hand the transport rate constant from membrane phase to receiving phase (k2) Ni(II) (2.7580 per hour) greater than Cd(II) (1.3790 per hour). The phase-to-phase transport of Ni(II) and Cd(II) was consecutive first order reaction.  Keywords : bulk liquid membrane, oxine, technique    
PENGARUH UDARA TERHADAP FOTOLISIS AIR OLEH SERBUK TiO2 DENGAN ADANYA KALIUM IODIDA Alif, Admin; Aziz, Hermansyah; Tetra, Olly Norita; Prima, Suci Mulya
Jurnal Riset Kimia Vol 3, No 2 (2010): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v3i2.28

Abstract

  ABSTRACT Hydrogen is one of the promising alternative energy sources which is environmentally-friendly. Amongs several methods that have been used to produce hydrogen is a photolysis base on photochemical reaction which has been choosen and applied for this work. In this system where water was photolyzed in the present of TiO2 powder as photocatalyst and potassium iodide as sacrificial agent. The sample was prepared by addition various potassium iodide concentrations and then each sample was treated in the present and absent of air. The sample was placed in a quartz reactor which was then illuminated by a Philips low pressure vapoured mercury lamp (λ = 254 nm) as light source for 7 hours. Produced gas volume was measured by a method based on the movement of soap bubbles. The results showed that the maximum gas volume obtained at 0.006 g/L TiO2 and 0.1 g/L KI concentration (in the present and absent of air) were applied. Furthermore, the maximum volume of hydrogen gas was produced at the present of air. In the present of air, dissolved oxygen accelerated H2 gas productions which act as oxidation agent and electron carrier to H+. Keywords: Photolysis, Photocatalyst, Titania, Hydrogen, Sacrificial agent
INHIBISI KOROSI BAJA RINGAN MENGGUNAKAN BAHAN ALAMI DALAM MEDIUM ASAM KLORIDA: Review Stiadi, Yeni; Arief, Syukri; Aziz, Hermansyah; Efdi, Mai; Emriadi, E.
Jurnal Riset Kimia Vol 10, No 1 (2019): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v12i2.321

Abstract

The corrosion of steel and its alloys is an important problem in industry, especially in acidic environments. Mild steel is one of the important alloys of iron which has many industrial applications because of its excellent mechanical properties, but mild steel is susceptible to corrosion. Corrosion problems need to be a concern and must be handled properly. Hydrochloric acid is widely used for pickling, cleansing, decomposition and metal etching, on the other hand also contributes to corrosion of metal surfaces. Plant extracts investigated the properties, mechanisms of adsorption and efficiency of inhibition as environmentally friendly corrosion inhibitors for various steel materials in different acidic media. The efficiency of corrosion inhibition of steel from plant extracts analyzed ranged from 72-98% and generally as a mixed-type inhibitor. Most of the inhibitors are adsorbed on the steel surface through a physisorption mechanism.