EFEKTIVITAS POLYVINYL ACETATE (PVAC) SEBAGAI MATRIKS PADA KOMPOSIT SAMPAH Masturi, Masturi; Mikrajuddin, Mikrajuddin; Khairurrijal, Khairurrijal
BERKALA FISIKA Vol 13, No 2 (2010): Berkala Fisika
Publisher : BERKALA FISIKA

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (234.552 KB)

Abstract

It was fabricated a composite using solid waste as filler and polyvinyl acetate (PVAc) as matrice. This work is as a solution of more serious solid waste problems. The solid waste used is paper waste and leaf one with their composition are 60% and 40% respectively. The crushed-solid waste then hot-pressed at 100 MPa of pressure and 150°C of temperature. Then, the compressive strength of composite before and after PVAc presence was investigated to get a composition in which the compressive strength is optimum.   Keywords: composite, solid waste, polyvinyl acetate, compressive strength.
EFFECT OF THICKNESS AND TEMPERATURE OF SIO2 LAYER ON LEAKAGE CURRENTS IN MOS CAPACITOR MATERIALS WITH HIGH DIELECTRIC CONSTANT BY INVOLVING THE CHARGE TRAP Noor, Fatimah A.; Masturi, Masturi; Abdullah, Mikrajuddin; Khairurrijal, Khairurrijal
Jurnal ILMU DASAR Vol 15 No 1 (2014)
Publisher : Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Jember

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (657.255 KB) | DOI: 10.19184/jid.v15i1.642

Abstract

Modeling of the leakage current in a field-effect transistor metal-oxide-semiconductor (MOSFET) with high dielectric material has been developed by taking into account the effect of charge traps formed at the interface of high-k material/SiO2. Transmittance calculated using Airy wave function approach and involving the anisotropic electron mass and the effect of coupling between transverse and longitudinal energy represented by the speed of the electrons in the metal gate. Transmittance obtained is then used to calculate the leakage current in the structure of n+Poly-Si/HfSiOxN/trap/SiO2/p-Si for oxide voltage variations, temperature, and thickness of the SiO2. From the calculation that the leakage current decreases with decreasing of oxide voltage and increasing of the thickness of the oxide layer of SiO2. Also obtained that the temperature of the device does not give a great influence on the change of leakage current. Keywords: Leakage current, electron speed, charge traps
MEREDUKSI PENGGUNAAN HANDPHONE SAAT PEMBELAJARAN MELALUI LAYANAN BIMBINGAN KELOMPOK TEKNIK BEHAVIOR CONTRACT Dina, Ariba Seila; Masturi, Masturi; Rahardjo, Susilo
Jurnal Prakarsa Paedagogia Vol 2, No 2 (2019): Desember 2019
Publisher : Universitas Muria Kudus

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24176/jpp.v2i2.4509

Abstract

Tujuan penelitian ini adalah : 1. Mendiskripsikan layanan bimbingan kelompok dengan teknik behavior contract dalam mereduksi penggunaan handphone saat pembelajaran pada siswa kelas X TKKR 1 Mejobo Kudus Tahun Pelajaran 2018/2019. 2. Untuk mengurangi perilaku penggunaan handphone setelah mendapat layanan bimbingan kelompok dengan teknik behavior contract dalam mereduksi penggunaan handphone saat pembelajaran pada siswa kelas X TKKR 1 SMK PGRI 1 Mejobo Kudus Tahun Pelajaran 2018/2019. Hasil penelitian diketahui penggunaan handphone saat pembelajaran peserta didik pada pra siklus memperoleh skor rata-rata 12 dengan kategori sering (SR), sedangkan hasil siklus I memperoleh skor rata-rata 13 dengan kategori kadang-kadang, pada siklus II memperoleh skor rata-rata 17 dengan kategori tidak pernah (TP).
SELF REGULATION SISWA DI ERA GLOBALISASI REFLEKSI BAGI GENERASI MILENIALS Sumarwiyah, Sumarwiyah; Masturi, Masturi; Afifah, An Nisa Nur; Dina, Ariba Seila
Jurnal Prakarsa Paedagogia Vol 1, No 2 (2018): Desember 2018
Publisher : Universitas Muria Kudus

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24176/jpp.v1i2.3441

Abstract

Self regulation is a process that activates thoughts, behaviors, and feelings that are continuous in an effort to achieve a set goal. Millennial generation is a group of young people born between 1980 and 2000 in very rapid technological developments. Reflection on self regulation in the millennial generation is very appropriate to implement, because by reflecting millennial generations it can be easier to improve selfregulation optimally. When millennials have positive regulations and are balanced with technological advances, they can form a generation that is a positive generation. By way of reflection selfregulation the millennial generation can control or manage themselves which includes cognitive, affective, and psychomotor aspects, so that it can become a millennial generation that can utilize social media well.
PEMASANGAN SENSOR GELOMBANG ULTRASONIK UNTUK APLIKASI ROBOT ANTI-BENTUR Masturi, Masturi; Sujarwata, Sujarwata
JURNAL ISTEK Vol 5, No 1-2 (2011): ISTEK
Publisher : JURNAL ISTEK

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Penelitian ini bertujuan untuk membangun sebuah mobil robot dan teknik pemasangan sensor gelombang ultrasonik untuk menghindari benturan. Teknik pemasangan sensor meliputi jarak sensor penerima ke pemancar gelombang ultrasonik dan panjang loop yang digunakan. Mengatur gerakan mobil robot secara otomatis dapat menghindari benturan dengan objek yang ada di depannya. Sistem otomasi pengaturannya menggunakan perangkat keras mikrokontroler Basic Stamp BS2SX buatan Parallax Inc Amerika, berupa IC PIC16C65 yang beroperasi pada tegangan 5 volt DC. Sedangkan perangkat lunaknya menggunakan bahasa pemrograman Pbasic. Program ditulis pada Basic Stamp Editor yang sudah diinstallkan pada PC, kemudian didownload ke EEPROM. Proses download program otomatis menghapus program sebelumnya sehingga program terakhir yang akan dieksekusi. Sensor gelombang ultrasonik yang digunakan dapat mendeteksi jarak objek terjauh 85 cm, sedangkan objek terdekat adalah 0,5 cm. Panjang loop yang dipasang pada mobil robot adalah 2 cm dan jarak antara transduser satu dengan yang lainnya 1,5 cm.Panjang loop yang dipasang pada mobil robot mempengaruhi jarak objek yang dapat dideteksi.
COUNSELOR ENCAPSULATION: SEBUAH TANTANGAN DALAM PELAYANAN KONSELING LINTAS BUDAYA Masturi, Masturi
JURNAL KONSELING GUSJIGANG Vol 1, No 2 (2015): Jurnal Konseling Gusjigang Desember 2015
Publisher : Universitas Muria Kudus

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24176/jkg.v1i2.407

Abstract

Counselor Encapsulation adalah kecenderungan konselor untuk mengungkung dirinya pada kebenaran budayanya sendiri sehingga cenderung bersikap resisten pada kebenaran budaya lain. Pelayanan Konseling Lintas Budaya membutuhkan kepekaan budaya dari konselor agar tidak terjadi bias pemaknaan substansi konseling. Oleh karena itu, kecenserungan konselor untuk melakukan enkapsulasi diri harus ditekan agar tidak muncul saat layanan konseling lintas budaya dilaksanakan.
PROSES CETAK BRIKET BERBAHAN LIMBAH KOLANG-KALING DENGAN TEKNOLOGI TEPAT GUNA Supriyadi, Supriyadi; Masturi, Masturi; J, Pratiwi D
Jurnal Abdimas Vol 19, No 2 (2015)
Publisher : Lembaga Penelitian dan Pengabdian Masyarakat (LP2M), Universitas Negeri Semarang

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Telah dilaksanakan kegiatan kepada masyarakat berupa pengembangan alat cetak briket di desa Jatireo kecamatan Gunungpati kodia Semarang. Latar belakang kegiatan ini adalah untuk mengatasi proses pembuatan briket pada saat dicetak, dimana hasil yang diperoleh belum padat sehingga lama nyala api belum sesuai yang diharapkan. Untuk mengatasi masalah tersebut telah dibuat alat pres yang digunakan untuk memberi beban briket sebelum dikeluarkan dari alat cetak. Hasil yang diperoleh menunjukkan adanya perbedaan ketebalan briket yang tidak dipres dengan yang dipres. Ketebalan briket tanpa menggunakan pres adalah 1 cm dan yang menggunakan alat pres 0,5 cm. Selain itu hasil uji pembakaran diperoleh laju pembakaran briket dari kulit kolang-kaling pada rentang 0.03-0.04 g/s. Hasil ini bersesuaian dengan briket dari jenis biomassa jenis lainnya seperti kayu, daun lain-lain dengan laju pembakarannya 0.03 g/s. Warna nyala api yang ditunjukkan ketika uji coba laboratorium adalah kuning kemerahan dan asapnya tidak menimbulkan gatal jika mengenai kulit.Kata kunci : briket, alat cetak, alat pres
PEMBUATAN BRIKET BERBAHAN LIMBAH KULIT KOLANG-KALING DI DESA JATIREJO GUNGPATI SEMARANG Supriyadi, Supriyadi; Masturi, Masturi; Mahardika, P.A.; Pratiwi, D.J.; Susilo, Susilo
Rekayasa Vol 12, No 1 (2014): Juli 2014
Publisher : Unnes Journal. Research and Community Service Institute, Semarang State University

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Community service activities have been carried out with the caption Accompaniment Leather Processing fro Being Gunungpati Jatirejo village Briquette in Semarang. Background This village was chosen for the reason that it has expanded economic activity that produces a variety of snack food products that is characteristic of this village. Program-related community service activities above, the Physics Department has undertaken preparatory activities carried out in the laboratories of Physics. In this preparatory activities have made a molding tool briquettes, briquette press equipment for compacting, testing and analysis of samples. The next activity is the implementation of the results on the field were done with lectures and practical approach. The results of the activities in the field generally indicates that the participants can make some sample briquettes. However, to further the process has not been analyzed, considering the current conditions do not allow the activity to heat up with the sun because of the rain.
PROSES CETAK BRIKET BERBAHAN LIMBAH KOLANG-KALING DENGAN TEKNOLOGI TEPAT GUNA Supriyadi, Supriyadi; Masturi, Masturi; D.J., Pratiwi
Rekayasa Vol 13, No 2 (2015): Desember 2015
Publisher : Unnes Journal. Research and Community Service Institute, Semarang State University

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Has carried out activities to the community in the form of the development of the printing press in the village briquettes Jatireo Gunungpati Kodia subdistrict in Semarang. The background of this activity is to address the process of making briquettes at the time of printing, where the results obtained are not crowded so long the flame is not as expected. To overcome these problems have created a tool that is used to press briquettes load prior to release of the molding tool. The results showed no difference in the thickness of the pressed briquettes are pressed. The thickness of the briquettes without using the press is 1 cm and 0.5 cm using a press. In addition, test results obtained by burning briquettes burning rate of the skin and fro in the range of 0.03 to 0.04 g/s. This result is consistent with the type of biomass briquettes from other types such as wood, leaves, etc. with 0.03 combustion rate g/s. The color of the flame indicated when laboratory testing is reddish yellow and the smoke does not cause itching when on the skin.
Pemanfaatan Limbah Daun Jambu dan Polimer Alami Getah Karet Sebagai Bahan Alternatif Furniture Damayanti, Heru; Masturi, Masturi; Yulianti, Ian
Jurnal Fisika Vol 5, No 1 (2015)
Publisher : Jurnal Fisika

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Limbah organik maupun anorganik seperti daun, kertas, sayuran, buah-buahan, styrofoam,dan plastik dapat digunakan sebagai sesuatu yang bermanfaat. Pada penelitian sebelumnya, sampah yang sering digunakan antara lain sampah styrofoam, sekam padi, kertas, plastik,dan serbuk kayu dapat dijadikan sebagai alternatif bahan bangunan, dan telah teruji kelebihannya, baik secara fisik maupun mekanik. Pada penelitian ini memanfaatkan sampah halaman yang kadang mengganggu dan tidak terkelola dengan baik, salah satunya adalah daun jambu. Komposit sampah daun jambu dapat digunakan sebagai bahan alternatif furniture seperti papan partikel yang berfungsi sebagai penyangga keyboard komputer, rak sepatu dan lain-lain. Daun jambu yang kering dibuat sebagai komposit dengan polimer alami getah pohon karet. Komposit dibuat dengan cara pencampuran sederhana (simple mixing) dengan perbandingan massa daun jambu dan getah karet masing–masing 5:1, 5:2, 5:3, 5:4 , 5:5 dan 5:6. Sampah daun kering yang sudah dihancurkan kemudian dipress dengan mesin pengepress  pada posisi berat 5 ton tekanan 39,81 MPa dan suhu kamar. Komposisi maksimum dari pencampuran komposit dengan polimer getah karet dapat diuji dengan melakukan uji kekuatan tekan. Kekuatan tekan yang paling baik menunjukkan bahwa komposit daun jambu dengan polimer getah karet layak untuk dijadikan sebagai bahan alternatif furniture pengganti kayu.