APLIKASI SINTESIS TiO2 NANOPARTIKEL DALAM DEGRADASI FOTOKATALITIK METIL JINGGA Husna, Isramil; Umar, Akrajas Ali; Ramli, Muhammad Adam
Sainstek : Jurnal Sains dan Teknologi Vol 10, No 1 (2018)
Publisher : IAIN Batusangkar

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (324.546 KB) | DOI: 10.31958/js.v10i1.1203

Abstract

The development in textile industry results in the increase of the use of non-organic materials in human life, such as the use of dyes that cannot be decomposed naturally, such as the use of artificial dyes in textile industry and other similar fields. This implies that if those artificial dye are not carefully managed, they will have a definite impact on the environment, such as water pollution where those substances contaminate clean water and therefore will be very dangerous for human daily needs of water for drinking, bathing and other needs. This in turn will cause various diseases in living things and pollute nature as well. The purpose of this study is to figure out the effect of methyl orange degradation by the addition of TiO2 photocatalyst. In this study, 10 ppm orange methyl solution were used, where 5 ml of orange methyl were dissolved in 5 ml of water then added with TiO2 and then irradiated with UV for 180 minutes. By calculating the degradation of methyl orange every 10 minutes, which was measured using a UV-Vis spectrophotometer. The finding shows that the longer the irradiation takes place, the more desirable degradation of methyl orange is desired. The results obtained from 180 minutes are absorbance values that are worth 0.8 down to 0.3.
EFEK KONSENTRASI Cu PADA STRUKTUR DAN SIFAT HANTARAN LISTRIK NANOPARTIKEL CuPt Imamora, Marjoni; R, Setia Erlila; Rahmi, Elvy; Maiyena, Sri; Umar, Akrajas Ali
Sainstek : Jurnal Sains dan Teknologi Vol 7, No 1 (2015)
Publisher : IAIN Batusangkar

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (492.139 KB) | DOI: 10.31958/js.v7i1.128

Abstract

The investigation of bimetallic CuPt Nanoparticles (CuPt NPs) with average diameters in the 196.7±98 nm range have been prepared by the Liquid phase deposition methods and synthesized directly on an indium tin oxide (ITO) substrate. CuPt NPs with  high surface defect grown on (ITO) surface were prepared via a simple immersion of the substrate into a solution contains 1 mM Potassium Hexachloro Platinate (K2PtCl6), 0.2 mM Anhydrous Copper (II) Sulfate (CuSO4) anhydrous, 0.01 M Sodium dodecyl sulfate (SDS) and 10 mM Formic acid for 4 h at room temperature. The modification of Cu2+ ion precursor play a role to determine the nanoparticles geometry obtained. The simultaneous reduction of metal ions leads to either a surface enriched with one component or an alloy type of structure depending on the bimetal composition. The bimetallic CuPt NPs dispersions are characterized by FESEM, EDX Mapping, XRD, HRTEM and XPS analysis.Key words: CuPt, Liquid phase deposition, Bimetallic CuPt NPs
Pengaruh Doping Palladium (Pd) Terhadap Lapisan TiO2 dengan Metoda LPD untuk Applikasi Fotoanoda Sel Surya DSSC Dahlan, Dahyunir; Dwipanur P.U, Andhika; Firmawati, Nini; Umar, Akrajas Ali
Jurnal Ilmu Fisika Vol 11, No 1 (2019): JURNAL ILMU FISIKA
Publisher : Jurnal Ilmu Fisika

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jif.11.1.13-17.2019

Abstract

Lapisan TiO2 yang didoping Pd dengan metode deposisi fase cair (Liquid Phase Deposition, LPD) telah dilakukan. Adapun tujuan sintesis lapisan tersebut adalah untuk mendapatkan lapisan yang terdiri dari nanoplate yang akan diaplikasikan untuk fotoanoda sel surya. Sebagai larutan prekursor digunakan 0,5 M (NH4)2TiF6 dengan variasi doping Pd adalah 0; 6.25; 12.50; 25,00 dan 50,00 mM. Penumbuhan lapisan dilakukan pada suhu 900°C selama 9 jam. Didapatkan berturut-turut energi gap adalah 3,20, 3,25, 3,18, 3,16, dan 3,10 eV. Karakterisasi FESEM menunjukkan bahwa lapisan yang dihasilkan terdiri dari partikel berbentuk nanoplate yang tersebar merata di permukaan substrat ITO. Luas nanoplate yang dihasilkan di bawah 100 μm2 dengan ketebalan beberapa nanameter. Karakterisasi I-V menunjukkan bahwa lapisan TiO2 yang didoping oleh Pd sangat berpotensi sebagai photoanode untuk elektroda sel surya DSSC (Dye Sensitized Solar Cell).Kata kunci:TiO2, Pd, DSSC, LPD, fotoanoda
Pengaruh Surfaktan Biner Cetil Trimetil Amonium Bromida (CTAB)- Hexametilen Triamin (HMT) pada Pembentukan Perak Nanorods menggunakan Katalis Natrium Hidroksida Noviyanti, Atiek Rostika; Hastiawan, Iwan; Umar, Akrajas Ali; Eddy, Diana Rakhmawaty; Abdilah, Gani
Al-Kimia Vol 5, No 1 (2017): June
Publisher : Study Program of Chemistry - Alauddin State Islamic University of Makassar

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.24252/al-kimia.v5i1.2843

Abstract

Nanoparticles have different physical properties and more interesting than that of bulk material. Nanoparticles are highly preferred for applications in various technologies as a catalyst, the raw material of electronic components, and as an antimicrobial agent. The aim of the research is synthesize of silver nanorods.  The effect of a binary surfactant CTAB-HMT on the morphology and homogeneity were investigated using UV/Vis spectrophotometer, TEM, and XRD. Base on the UV/Vis spectra and TEM morphology, silver nanoparticles have two types, spherical and rods shapes.  The best product of nanorods was obtained  at the composition of CTAB 0.15 M : HMT 0.15 M. The structure of nanorods obtained were face center cubic (fcc).
PENUMBUHAN DAN KARAKTERISASI NANOPARTIKEL PERAK PADA SUBSTRAT PADAT Yani, Rizky Ardie; ', Iwantono; Umar, Akrajas Ali
Jurnal Online Mahasiswa (JOM) Bidang Matematika dan Ilmu Pengetahuan Alam Vol 1, No 2 (2014): Wisuda Oktober 2014
Publisher : Jurnal Online Mahasiswa (JOM) Bidang Matematika dan Ilmu Pengetahuan Alam

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Silver nanoparticles have been successfully grown on solid substrate. The growth of the particles used wet chemical  method which consisted of two steps, seeding and growing steps. The silver nanoparticle growth was carried out by two variations which were surfactant’s concentration and ascorbic acid’s volume.  The UV-Vis spectrum profile of the samples described that the  growth of silver nanoparticles of spherical shape was dominated on the ITO, represented as a sharp single peak of the absorption spectra. Its characterization measured by XRD showed that silver nanoparticles had grown on the substrate with crystal orientation (1 1 1) and (2 0 0). The FESEM images depicted that the shape of silver nanoparticles was a spherical shape with their uniform diameter size of 300-650 nm.
Sintesis Nanopartikel Titanium Dioksida Didoping Rhutenium Bajili, Abdil; Dahlan, Dahyunir; Umar, Akrajas Ali
Jurnal Ilmu Fisika Vol 8, No 2 (2016): JURNAL ILMU FISIKA
Publisher : Jurnal Ilmu Fisika

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jif.8.2.54-59.2016

Abstract

Nanopartikel titanium dioksoda (TiO2) yang didoping ruthenium (Ru/TiO2) ditumbuhi dengan menggunakan metode penumbuhan Liquid Phase Deposition (LPD) telah berhasil dilakukan. Konsentrasi doping ruthenium yang digunakan adalah 2,5 mM. Variasi lama waktu penumbuhan dilakukan selama 3 jam, 5 jam, 7 jam dan 10 jam. Kemudian dilakukan karakterisasi Ultraviolet-visible, fotoelektron sinar-x dan teknik difraksi sinar-x. Energi gap yang didapatkan dengan waktu penumbuhan 3 jam dan 5 jam adalah 3,22 eV dan 3,28 eV. Sedangkan waktu penumbuhan 7 jam dan 10 jam adalah 3,16 eV dan 3,29 eV. Morfologi dari Ru/TiO2 bersifat nanopori dengan fasa adalah anatase. Kata kunci: Liquid Phase Deposition (LPD), nanopartikel Ru/TiO2, doping ruthenium, fase anatase. 
Pengaruh Lama Penumbuhan Titanium Dioksida Didoping Copper Terhadap Energi Gap Berli, Ade Usra; Dahlan, Dahyunir; Umar, Akrajas Ali
Jurnal Ilmu Fisika Vol 8, No 2 (2016): JURNAL ILMU FISIKA
Publisher : Jurnal Ilmu Fisika

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jif.8.2.60-63.2016

Abstract

Deposisi lapisan TiO2 didoping Cu telah berhasil ditumbuhkan dengan menggunakan metoda Liquid Phase Deposition (LPD). Lapisan TiO2-Cu dibuat dengan menggunakan material Ammonium hexafluorotitanate ((NH4)2TiF6), Copper (II) Nitrate hydrate (Cu(NO3)2·xH2O), dan Hexamethylen tetramine (C6H12N4). Dalam penelitian ini dilakukan variasi lama penumbuhan lapisan yaitu 3 jam, 5 jam, 7 jam dan 10 jam. Lapisan TiO2-Cu dikarakterisasi menggunakan Spektrometri Ultraviolet-Visible (UV-Vis) untuk menentukan energi gap melalui spektra difusi reflektansi. Hasil energi gap yang diperoleh pada lapisan TiO2-Cu dengan variasi lama penumbuhan yaitu antara 3,26-3,30 eV.Kata kunci: Titanium dioksida (TiO2), Liquid Phase Deposition (LPD) dan doping 
PENGARUH DOPING PALLADIUM (PD) TERHADAP LAPISAN TIO2 DENGAN METODE LPD UNTUK APPLIKASI FOTOANODA SEL SURYA DSSC Dwipanur, Andhika; Dahlan, Dahyunir; Firmawati, Nini; Umar, Akrajas Ali
Jurnal Ilmu Fisika Vol 12, No 1 (2020): JURNAL ILMU FISIKA
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jif.12.1.6-10.2020

Abstract

Lapisan TiO2 yang didoping Pd dengan metode deposisi fase cair (Liquid Phase Deposition, LPD) telah dilakukan. Adapun tujuan sintesis lapisan tersebut adalah untuk mendapatkan lapisan yang terdiri dari nanoplate yang akan diaplikasikan untuk fotoanoda sel surya. Sebagai larutan prekursor digunakan 0,5 M (NH4)2TiF6 dengan variasi doping Pd adalah 0; 6.25; 12.50; 25,00 dan 50,00 mM. Penumbuhan lapisan dilakukan pada suhu 900°C selama 9 jam.Didapatkan berturut-turut energi gap adalah 3,20; 3,25; 3,18; 3,16; dan 3,10 eV. Karakterisasi FESEM menunjukkan bahwa lapisan yang dihasilkan terdiri dari partikel berbentuk nanoplate yang tersebar merata di permukaan substrat ITO. Luas nanoplate yang dihasilkan di bawah 100 ?m2 dengan ketebalan beberapa nanometer. Karakterisasi-karakterisasi ini menunjukkan bahwa lapisan TiO2 yang didoping oleh Pd sangat berpotensi sebagai photoanode untuk elektroda sel surya DSSC (Dye Sensitized Solar Cell).