Analysis of Optical Properties TiO2, ZnO, TiO2: ZnO Thin Films Deposited On Glass Substrate Using Sol-Gel Spray Coating Method And Application For Degradation Of Dye Liquids.

AMANANTI, WILDA - (Unknown)
amananti, wilda (Unknown)



Article Info

Publish Date
31 Dec 2017

Abstract

TiO2, ZnO and TiO2: ZnO Thin film have been deposited on glass substrate by sol-gel method of Spray Coating Technique. TiO2: ZnO and ZnO can form well above the glass substrate. The precursor solution of TiO2 and TiO2: ZnO is deposited using sol-gel method of Spray Coating Technique. Zinc acetate dehydrate (Zn (COOCH3) 2 .2H2O was dissolved into an isopropanol ((CH3) 2CHOH) solvent and then added monoethanolamine (MEA: HOCH2CH2NH2) .The solution was stirred at 70oC until a clear and homogeneous solution was obtained.Titanium Tetraisopropoxide (TTIP) 0 , 73 ml was dissolved into 4.27 ml of isopropanol and 20 ml of ethanol, after which the solution was titrated with 5 ml of ethanol, 3.4 ml acetic acid and 0.26 ml H2O, then stirred on hot plate stirrer at room temperature ( Further, the ZnO, TiO2 and TiO2: ZnO precursor gels were sprayed on a glass substrate that was heated at a temperature of 450 ° C. The results of the TiO2 thin film bandgap energy measurement were 3.58 eV, ZnO thin films of 3.08 eV, and a thin layer of TiO2: ZnO of 3.06 eV Doped photodegradation dye Direct blue 10 ppm using UV-reactor The highest percentage of degradation is found in TiO2: ZnO thin film

Copyrights © 2017






Journal Info

Abbrev

JNSMR

Publisher

Subject

Description

Scientific articles dealing with fundamental sciences, material sciences, mathematics, materials characterization, etc. are particularly welcome. The journal encompasses research articles, original research report, reviews, short communications and scientific commentaries in fundamental sciences and ...